Water-soluble flux 703 Introduction

Unibright 703 lead-free water-soluble flux is specially designed for automatic welding equipment with a water washing process. This product does not contain rosin and has little corrosion to the metal surface of the plate and welding equipment; the welding process produces less smoke and no irritating odor; the water cleaning effect is good, the solder joints are full and bright, and the solder joint strength is high. For high-quality and stable welding operations in electronic product production, this product can meet the requirements.

Enquire now

Sample test

Water-soluble flux 703 Product Features

? This product does not contain rosin and has little corrosion to the metal surface of the board and welding equipment.
? The welding process produces less smoke and no irritating odor.
? The solder joints are full and bright, with high strength.
? Good water cleaning effect, combined with spray/ultrasonic cleaning, can quickly clean and achieve extremely low ion residue.
? For high-quality and stable welding operations in electronic product production, this product can meet the requirements.

Water-soluble flux 703 Applicable process

The application method of Unibright 703 lead-free water-soluble flux can be coating or impregnation, with good process adaptability.

Apply for product information

Water-soluble flux 703 Application

? The service life of soldering flux varies slightly due to process conditions. When the flux is not in working condition, it should be kept in a sealed container as much as possible to avoid solvent evaporation.

? When it is necessary to replace expired flux, the flux container should be thoroughly cleaned before replacing with a new flux.

? Pre heating after application of flux can fully leverage the advantages of Heming 703 lead-free water-soluble flux. It is recommended that the preheating temperature should reach 100-150 ℃ on the PCB board or component welding surface after preheating.

? Using hot water at 50-60 ℃ combined with spray/ultrasonic cleaning can achieve the minimum ion residue without the need for any cleaning agent.